Abstract The vinyl ester resins and natural composites have emerged as a suitable alternative in tribological application due to mechanical behavior, which relates to the conversion of the double bonds. During tribological test the permanent contact between polymeric sample and counterpart can increase the temperature affecting the crosslinking of the samples. These variations have direct implications in the curing rate and the global conversion. In this work, the FTIR evaluation is used to evaluate possible changes on the global conversion of vinyl ester and their composites reinforced with Musaceae fiber bundles and cured using two hardeners, after a specific tribological test. Increments around 15% on global conversion of styrene double bonds were observed for neat matrix and composites using both hardeners, suggesting that during tribology test some alterations on resin structure takes place. These results open alternatives to manipulate the curing conditions in order to control the tribological behavior.

Neste trabalho são apresentados os resultados da síntese de nanocompósitos baseados em amido termoplástico (TPS) reforçado com nanofitas de celulose bacteriana (BC). A síntese foi feita por fermentação in situ e formação de ligações cruzadas. A fermentação para a obtenção das nanofitas foi conduzida por sete dias empregando a bactéria colombiana nativa Gluconacetobacter medellinenses; os nanocompósitos foram plasticizados com glicerol e as ligações cruzadas foram formadas com ácido cítrico. Os nanocompósitos obtidos depois destes sete dias de fermentação foram caracterizados por análise termogravimétrica (TGA), espectroscopia na região do infravermelho com transformada de Fourier com refletância total atenuada (FTIR-ATR) e microscopia electrônica de varredura (SEM). Observou-se que, ao longo da fermentação, a porcentagem de reforço nos nanocompósitos permaneceu constante. Os novos nanocompósitos TPS/BC apresentaram uma forte adesão interfacial e uma maior estabilidade térmica e aquosa, assim como propriedades mecânicas melhoradas. Os resultados obtidos aumentam consideravelmente as possibilidades de aplicação do amido na indústria de embalagens.

In this paper, a nanocomposite based on thermoplastic starch (TPS) reinforced with bacterial cellulose (BC) nanoribbons was synthesized by in situ fermentation and chemical crosslinking. BC nanoribbons were produced by a Colombian native strain of Gluconacetobacter medellinensis; the nanocomposite was plasticized with glycerol and crosslinked with citric acid. The reinforcement percentage in the nanocomposites remained constant throughout the fermentation time because of the TPS absorption capability of the BC network. Nanocomposites produced after fermentation for seven days were characterized using thermogravimetric analysis (TGA); Fourier transformed infrared spectroscopy with attenuated total reflectance (FTIR-ATR), mechanical testing and scanning electron microscopy (SEM). The new TPS/BC nanocomposites exhibit strong interfacial adhesion, improved thermal behavior, water stability and enhanced mechanical properties. These findings support the applications of starch in the packaging industry.

No presente trabalho, biofilmes condutores foram sintetizados através de soluções de 100 mL de água com 3 g de amido de mandioca (Manihot esculenta Crantz) e quantidades diferentes de glicerina, glutaraldeído, polietilenoglicol e perclorato de lítio. Estes filmes foram caracterizados por espectroscopia de impedância eletroquímica (EIS), microscopia eletrônica de varredura (SEM), espectrometria de reflexão total atenuada no infravermelho com transforma de Fourier (ATR-FTIR), termogravimetria (TG). Os resultados mostraram que os biofilmes com quantidades mais elevadas de perclorato de lítio possuem valores maiores de condutividade e as diferenças morfológica e molecular foram observadas como sendo um resultado das proporções adicionadas dos compostos em cada uma das rotas de preparação

In the current work, conductor biofilms were synthesized by means of solutions of 100 mL of water with 3 g of starch from cassava (Manihot esculenta Crantz) and different amounts of glycerin, glutaraldehyde, polyethyleneglycol and lithium perchlorate. These biofilms were characterized through electrochemical impedance spectroscopy (EIS), scanning electronic microscopy (SEM), attenuated total reflectance Fourier transform infrared spectroscopy (ATR‑FTIR) and thermogravimetry (TG). Results showed that biofilms with higher amount of lithium perchlorate portray higher values of conductivity and morphological and molecular differences could be observed as a result of the added proportions of the compounds in each one of the trials.